University of New South Wales researchers have identified four failure modes caused by damp heat in heterojunction solar panels with a glass-back sheet configuration. The failures could result in power losses ranging from 5% to 50%. A research team from the University of New South Wales (UNSW) has investigated failure modes in heterojunction (HJT) solar modules with glass-backsheet configurations. "We have identified four failure modes in the silicon heterojunction glass-backsheet module which has the potential to result in a power loss of up to 50% following damp heat testing," researcher Chandany ...Den vollständigen Artikel lesen ...